PA66 RP003沙伯基礎創新內部潤滑含有機硅PTFE尼龍66塑料（18024445500）
Also known as:LNP™LUBRICOMP™Compound RL-4530
Product reorder name:RP003
LNP LUBRICOMP RP003 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, break
490
kgf/cm²
ASTM D 638
Tensile Strain, yield
4.6
%
ASTM D 638
Tensile Strain, break
4.7
%
ASTM D 638
Tensile Modulus, 50 mm/min
28100
kgf/cm²
ASTM D 638
Flexural Stress
700
kgf/cm²
ASTM D 790
Flexural Modulus
21000
kgf/cm²
ASTM D 790
Tensile Stress, yield
55
MPa
ISO 527
Tensile Stress, break
55
MPa
ISO 527
Tensile Strain, yield
4.7
%
ISO 527
Tensile Strain, break
4.7
%
ISO 527
Tensile Modulus, 1 mm/min
2960
MPa
ISO 527
Flexural Stress
85
MPa
ISO 178
Flexural Modulus
3000
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
38
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
3
cm-kgf/cm
ASTM D 256
Instrumented Impact Energy @ peak, 23°C
14
cm-kgf
ASTM D 3763
Multiaxial Impact
9
cm-kgf
ISO 6603
Izod Impact, unnotched 80*10*4 +23°C
26
kJ/m²
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
4
kJ/m²
ISO 180/1A
THERMAL
Value
Unit
Standard
HDT, 0.45 MPa, 3.2 mm, unannealed
201
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
59
°C
ASTM D 648
CTE, -40°C to 40°C, flow
9.E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
9.54E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
9.1E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
9.6E-05
1/°C
ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
221
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
66
°C
ISO 75/Af
PHYSICAL
Value
Unit
Standard
Density
1.27
g/cm³
ASTM D 792
Moisture Absorption, 50% RH, 24 hrs
0.6
%
ASTM D 570
Wear Factor Washer
10
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
Dynamic COF
0.22
-
ASTM D 3702 Modified
Static COF
0.16
-
ASTM D 3702 Modified
Density
1.27
g/cm³
ISO 1183
Source GMD, last updated:2007/08/02
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
供應的沙伯基礎PA66塑料如下：
LNP™ LUBRICOMP Compound
Grades
Description
RA004
Internally Lubricated Nylon 66 compound containing Aramid.
RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.
RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.
RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.
RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.
RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.
RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:
RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.
RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.
RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.
RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,
RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.
RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.
RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s). |