PA66 RN001S沙伯基礎創新內部潤滑熱穩定含二硫化鉬聚酰胺66尼龍塑料（18024445500）
Also known as:LNP™LUBRICOMP™Compound R- HS
Product reorder name:RN001S
LNP LUBRICOMP RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yield
850
kgf/cm²
ASTM D 638
Tensile Stress, break
850
kgf/cm²
ASTM D 638
Tensile Strain, yield
2.9
%
ASTM D 638
Tensile Strain, break
3.8
%
ASTM D 638
Tensile Modulus, 50 mm/min
42100
kgf/cm²
ASTM D 638
Flexural Modulus
35100
kgf/cm²
ASTM D 790
Tensile Stress, yield
69
MPa
ISO 527
Tensile Stress, break
69
MPa
ISO 527
Tensile Strain, yield
2
%
ISO 527
Tensile Strain, break
42.2
%
ISO 527
Tensile Modulus, 1 mm/min
3910
MPa
ISO 527
Flexural Stress
107
MPa
ISO 178
Flexural Modulus
3400
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
113
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
2
cm-kgf/cm
ASTM D 256
Instrumented Impact Energy @ peak, 23°C
23
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
53
kJ/m²
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
2
kJ/m²
ISO 180/1A
THERMAL
Value
Unit
Standard
HDT, 0.45 MPa, 3.2 mm, unannealed
231
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
76
°C
ASTM D 648
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
223
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
301
°C
ISO 75/Af
PHYSICAL
Value
Unit
Standard
Density
1.16
g/cm³
ASTM D 792
Wear Factor Washer
103
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
Dynamic COF
0.75
-
ASTM D 3702 Modified
Static COF
0.55
-
ASTM D 3702 Modified
Density
1.17
g/cm³
ISO 1183
Source GMD, last updated:2008/09/24
Processing
Parameter
Injection Molding
Value
Unit
Drying Temperature
80
°C
Drying Time
4
hrs
Maximum Moisture Content
0.15 - 0.25
%
Melt Temperature
275 - 290
°C
Front - Zone 3 Temperature
295 - 305
°C
Middle - Zone 2 Temperature
280 - 295
°C
Rear - Zone 1 Temperature
265 - 275
°C
Mold Temperature
80 - 95
°C
Back Pressure
0.2 - 0.3
MPa
Screw Speed
30 - 60
rpm
Source GMD, last updated:2008/09/24
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
供應的沙伯基礎PA66塑料如下：
LNP™ LUBRICOMP Compound
Grades
Description
RA004
Internally Lubricated Nylon 66 compound containing Aramid.
RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.
RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.
RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.
RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.
RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.
RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:
RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.
RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.
RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.
RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.
RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,
RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.
RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.
RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).
RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.
RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.
RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s). |