PA6 BKV 15 H3.0 DUS008 000000德國朗盛Durethan 15%玻纖增強熱老化穩定尼龍6塑料（18024445500）

PA 6, 15 % glass fibers, injection molding, heat-aging stabilized



ISO Shortname: ISO 1874-PA6, GHR, 14-070, GF15

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.35　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.60　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.15　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.15　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6500 3100
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 130 65
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3 12
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 50 100
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 45 45
Izod impact strength 23 °C kJ/m² ISO 180-1U 45 85
Izod impact strength -30 °C kJ/m² ISO 180-1U 40 40
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 10
Flexural modulus 2 mm/min MPa ISO 178-A 5500 3100
Flexural strength 2 mm/min MPa ISO 178-A 205 110
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.3 8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 180 80

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 220　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 195　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.3　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1